Hydrocarbon conversion processes using non-zeolitic molecular sieve catalysts

ABSTRACT

Hydrocarbon conversion process in which a feedstock is contacted with a non zeolitic molecular sieve to remove most, if not all, of the halogen contained in the catalyst. The halogen may be removed by one of several methods. One method includes heating the catalyst in a low moisture environment, followed by contacting the heated catalyst with air and/or steam. Another method includes steam-treating the catalyst at a temperature from 400° C. to 1000° C. The hydrocarbon conversion processes include the conversion of oxygenates to olefins, the conversion of oxygenates and ammonia to alkylamines, the conversion of oxygenates and aromatic compounds to alkylated aromatic compounds, cracking and dewaxing.

[0001] This application claims priority to U.S. patent application Ser. No. 09/891674 filed June 2001, the entire disclosure of which is incorporated herein by reference.

FIELD OF THE INVENTION

[0002] The present invention relates to methods of removing halogen from non-zeolitic, molecular sieve catalysts, the catalysts produced from such methods, and the use of such catalysts in hydrocarbon conversion processes.

BACKGROUND OF THE INVENTION

[0003] Molecular sieve catalysts used in a fluidized-bed reactor or a riser reactor will typically have an average particle diameter from 40 μm to 300 μm. Catalyst particle size within this range is needed for proper fluidization as well as to efficiently separate the catalyst from the gaseous products in a cyclone separator. To maintain the desired catalyst diameter the molecular sieve is formulated with other materials. Dilution of the molecular sieve with these materials is also used to control the rate of reaction, control the temperature of the reactor and regenerator, and to stabilize and protect the molecular sieve.

[0004] Formulated molecular sieve catalysts present a problem not found in other types of industrial catalysts, that is, how to maintain the physical integrity of the molecular sieve catalyst during the fluidized cyclic process of reaction, separation, and regeneration. The cycles of reaction, separation, and regeneration are carried out at high temperatures and high flow rates. Collisions and abrasions between catalyst particles, between the catalyst particles and reactor walls and between the catalyst particles and other parts of the unit tend to cause physical breakdown of the original catalyst into smaller catalyst particles known as fines. This physical breakdown is referred to as catalyst attrition. The fines usually have particle diameters smaller than 20 microns—much smaller than the original catalyst particles. Catalysts with higher attrition resistance are desirable because, among other reasons, fewer fines are generated for disposal, less environmental impact is caused by unrecoverable airborne particulates, optimal fluidized conditions are maintained, operating costs are lower, and less replacement catalyst is required.

[0005] Molecular sieve catalysts are formed by various methods, for example, by spray drying or extruding a slurry containing the molecular sieve and the other catalyst components. The catalysts are formed by mixing the zeolitic molecular sieve with one or more binding agents such as one or more types of alumina and/or silica. Matrix materials, typically clays, are also added and serve as diluents to control the rate of the catalytic reaction, and to facilitate heat transfer during many stages of the process. In U.S. Pat. No. 5,346,875 to Wachter et al. zeolite-Y (21.8 wt %) is mixed with Kaolin clay (14.5 wt %), silica sol (48.3 wt %), and Reheis chlorhydrol (15.4 wt %) to form a slurry which is then spray dried and calcined. A conventional calcination procedure was used; heating at 550° C. in air for 2 hours.

[0006] Non-zeolitic, molecular sieve catalysts are known to convert oxygenates, particularly methanol, to light olefins. The oxygenate to olefin process includes separate processing zones for conducting the catalytic reaction, product-catalyst separation, and catalyst regeneration. The produced olefin and other hydrocarbon products are separated from the catalyst particles in a separator, suitably a cyclone separator. A portion of the catalyst is recovered from the separator and passed to a regenerator. In the regenerator the non-zeolitic molecular sieve catalyst contacts a combusting gas, e.g. air, at a temperature sufficient to burn off carbon deposits, commonly referred to a coke, that accumulate on the surface and in the pores of the catalyst. The regenerated catalyst is then returned to the oxygenate conversion reactor.

[0007] In this process, the non-zeolitic molecular sieve catalyst is subjected to great mechanical stresses. As the catalyst is transferred from the reaction zone to cyclone separators, to regenerators, and finally back to the reaction zone the catalyst will tend to disintegrate into catalyst fines. These catalyst fines must be removed from the reactor process and discarded. No matter how resistant the catalyst is to attrition, eventually the oxygenate to olefin process will break down the non-zeolitic molecular sieve catalyst because the catalyst moves through the system at such high speeds. The resistance of the catalyst to attrition is an important property of the catalyst.

[0008] In PCT Publication No. WO 99/21651 to Wachter et al. and U.S. Pat. No. 4,973,792 to Lewis et al., silicoaluminophosphate (SAPO) molecular sieve catalysts were produced by preparing a slurry containing SAPO-34, Kaolin clay, and Reheis chlorhydrol. The slurry was then directed to a spray dryer to form catalyst particles with the desired size. The spray dried catalysts were calcined, however the conditions of the calcination were stated to be not critical.

[0009] In U.S. Pat. Nos. 5,248,647 and 5,095,163 to Barger et al. SAPO molecular sieve is mixed with an aqueous silica sol and spray dried. The spray dried catalyst is mixed with an aqueous solution of ammonium sulfate at 60° C. three times, then washed with water and dried at 100° C. The dried, ion-exchanged catalyst is then calcined in air at 550° C. for over 3.3 hours and then the temperature is lowered to ambient room temperature over a period of 2 hours. A portion of this catalyst is then contacted with steam at 725° C. or 750° C. for 10 hours. Steam treatment following calcination is shown to increase catalyst life, increase selectivity to ethylene and propylene, and decrease selectivity to propane.

[0010] If SAPO molecular sieve catalysts are ever going to be used commercially to convert oxygenates to olefins, catalysts with greater attrition properties are needed. For this reason, the Applicants' sought to develop SAPO catalysts with a relatively high resistance to attrition.

SUMMARY OF THE INVENTION

[0011] The present invention is directed to methods of removing a portion of the halogen present in non-zeolitic molecular sieve catalysts. One embodiment of removing halogen includes heating the catalyst in a low moisture environment at a temperature from about 400° C. to about 1000°, and contacting the heated catalyst with steam at a temperature from about 400° C. to about 1000° C. to produce a steam-treated catalyst. Preferably, the low moisture environment contains less than 5% by volume, more preferably less than 1% by volume, water. The steam treatment can take place in an oxygen environment. Also, it is preferred that the steam treatment take place in an environment containing at least 10% by volume water. In the preferred embodiment, the steam treatment can remove from about 50% to about 99% by weight, more preferably from about 90% to about 99% by weight, of halogen from the heated catalyst. The method can be used to remove halogen from silicoaluminophosphate and/or aluminophosphate molecular sieve selected from the group consisting of SAPO-5, SAPO-8, SAPO-11, SAPO-16, SAPO-17,

[0012] SAPO-18, SAPO-20, SAPO-31, SAPO-34, SAPO-35, SAPO-36, SAPO-37, SAPO-40, SAPO-41, SAPO-42, SAPO-44, SAPO-47, SAPO-56, ALPO-5, ALPO-11, ALPO-18, ALPO-31, ALPO-34, ALPO-36, ALPO-37, ALPO-46, the metal containing forms of each thereof, or mixtures thereof.

[0013] In another embodiment, a portion of the halogen can be removed from a non zeolitic molecular sieve catalyst by heating the catalyst in an oxygen environment at a temperature from about 400° C. to about 1000° C. to produce a heated catalyst, and contacting the heated catalyst with steam at a temperature from about 400° C. to about 1000° C. Preferably, the oxygen environment contains greater than about 10% by volume oxygen. It is also preferred, that the steam treatment take place in an environment containing at least about 10% by volume water. In many cases, the halogen to be removed will be chlorine, and preferably from about 70% to about 99% by weight, more preferably from about 90% to about 99% by weight, of the chlorine will be removed from the heated catalyst.

[0014] In another embodiment, a portion of the halogen can be removed from a non zeolitic molecular sieve catalyst by calcining the catalyst in an environment containing steam at a temperature from about 400° C. to about 1000° C., preferably from about 500° C. to about 800° C., and more preferably from about 550° C. to about 700° C., to remove from about 70% to about 99.99% by weight of the halogen from the catalyst. If the halogen to be removed from the catalyst is chlorine, the likely source of the chlorine is aluminum chlorhydrol that is used to produce the catalyst. The environment can contain from 5% to about 10% by volume water, or at least 10% by volume, water. The environment can further contain air, nitrogen, helium, flue gas, or any combination thereof.

[0015] In one embodiment, the catalyst is heated in a low-moisture environment at a temperature of from about 400° C. to about 1000° C. to remove at least about 50% by weight of the halogen in the catalyst prior to steam treatment. Preferably, the low moisture environment contains less than about 5% by volume, more preferably less then about 1% by volume, water. Also, the steam-treated catalyst can optionally be heated in an oxygen environment that contains greater than about 5% by volume oxygen.

[0016] In another embodiment, a portion of the halogen can be removed from a silicoaluminophosphate molecular sieve catalyst by heating the catalyst in a low moisture environment at a temperature from 400° C. to about 1000° C. to remove at least about 50% by weight of the chlorine from the catalyst, followed by contacting the heated catalyst in a second calcination environment containing about 5% to about 10% by volume water at a temperature from 400° C. to about 1000° C. Preferably, the low moisture environment contains less than about 1% by volume water.

[0017] The invention is also directed to a catalyst containing a non zeolitic molecular sieve, inorganic oxide matrix, and matrix material, wherein the catalyst contains from about 10 ppmw to about 600 ppmw by weight halogen. Generally, the halogen is chlorine, and the catalyst will contain from about 10 ppmw to about 200 ppmw, preferably from about 10 ppmw to about 80 ppmw, chlorine. It is also preferred that the catalyst have a GAL Index of less than about 5, more preferably less than about 3, most preferably less than about 2. The non-zeolitic molecular sieve in the catalyst is preferably selected from SAPO-5, SAPO-8, SAPO-11, SAPO-16, SAPO-17, SAPO-18, SAPO-20, SAPO-31, SAPO-34, SAPO-35, SAPO-36, SAPO-37, SAPO-40, SAPO-41, SAPO-42, SAPO-44, SAPO-47, SAPO-56, ALPO-5, ALPO-11, ALPO-18, ALPO-31, ALPO-34, ALPO-36, ALPO-37, ALPO-46, the metal containing forms of each thereof, or mixtures thereof. Preferably, the catalyst contains about 20% to about 45% by weight, more preferably from about 25% to about 42% by weight, non-zeolitic molecular sieve, about 5% to about 20% by weight, more preferably about 8% to about 15% by weight, of inorganic oxide matrix, and about 20% to about 70% by weight, more preferably from about 40% to about 60% by weight, matrix material. In the preferred embodiment, the inorganic oxide matrix contains an aluminum oxide matrix that is formed from the heat treatment of aluminum chlorhydrol.

[0018] The present invention also relates to hydrocarbon conversion processes in which a feedstock is contacted with a non zeolitic catalyst from which halogen has been removed. More specifically, the present invention relates to a hydrocarbon conversion process comprising the steps of (a) introducing a feedstock to a reactor system in the presence of a catalyst comprising a non zeolitic molecular sieve, inorganic oxide matrix, and matrix material, wherein the catalyst contains from 10 ppm to 600 ppm by weight halogen; (b) withdrawing from the reactor system an effluent stream; and (c) passing the effluent gas through a recovery system recovering at least the one or more conversion products.

[0019] In another embodiment, the present invention relates to a hydrocarbon conversion process comprising the steps of: (a) providing a halogen-containing non-zeolitic molecular sieve catalyst; (b) heating the catalyst in a low moisture environment at a temperature from 400° C. to 1000° C.; (c) contacting the heated catalyst with steam at a temperature from 400° C. to 1000° C. to produce a steam-treated catalyst; (d) introducing a feedstock to a reactor system in the presence of the steam-treated catalyst obtained at step (c); (e) withdrawing from the reactor system an effluent stream; and (f) passing the effluent gas through a recovery system recovering at least the one or more conversion products.

[0020] In another embodiment, the present invention relates to a hydrocarbon conversion process comprising the steps of (a) providing a halogen-containing non-zeolitic molecular sieve catalyst; (b) heating the catalyst in an oxygen environment at a temperature from 400° C. to 1000° C.; (c) contacting the heated catalyst with steam at a temperature from 400° C. to 1000° C. to produce a steam-treated catalyst; (d) introducing a feedstock to a reactor system in the presence of the steam-treated catalyst obtained at step (c); (e) withdrawing from the reactor system an effluent stream; and (f) passing the effluent gas through a recovery system recovering at least the one or more conversion products.

[0021] In a further embodiment, the present invention relates to a hydrocarbon conversion process comprising the steps of (a) providing a halogen-containing non-zeolitic molecular sieve catalyst; (b) heating the catalyst in an environment containing steam at a temperature from 400° C. to 1000° C.; (c) removing from 70% to 99.99% by weight of the halogen from the catalyst, thereby producing a steam-treated catalyst; (d) introducing a feedstock to a reactor system in the presence of the steam-treated catalyst obtained at step (c); (e) withdrawing from the reactor system an effluent stream; and (f) passing the effluent gas through a recovery system recovering at least the one or more conversion products.

[0022] In each of the preceding embodiments, the present invention is applicable to a wide range of processes including those in which the feedstock comprises one or more oxygenates, ammonia, aromatic compounds, or mixtures thereof, which are converted to olefins, alkylamines or alkylated aromatic compounds. The invention is also applicable for feedstock cracking and dewaxing.

BRIEF DESCRIPTION OF THE DRAWING

[0023] The present invention will be better understood by reference to the Detailed Description of the Invention when taken together with the attached drawing, wherein FIG. 1 is a schematic representation of one embodiment for removing chlorine from a formed catalyst.

DETAILED DESCRIPTION OF THE INVENTION

[0024] To produce non-zeolitic molecular sieve catalyst with a relatively high resistance to attrition, an inorganic oxide sol that contains halogen can be used. A preferred route to produce non-zeolitic molecular sieve catalyst is to use an alumina sol that contains chlorine, more preferably aluminum chlorhydrol, as a binder. The inorganic oxide sol functions as a “glue” which binds the catalyst components together. However, using an inorganic oxide sol that contains halogen presents a problem not associated with the use of halogen-free binders. A portion of the halogen from the inorganic oxide sol remains in the formed catalyst. It is desirable to remove most, if not nearly all, of the halogen from the catalyst before the catalyst is used in the oxygenate to olefin process. If most of the halogen is not removed from the catalyst, halogen-containing acids will form in the oxygenate to olefin reactor. Over time, the released acid will corrode the oxygenate to olefin reactor and other process units. While the invention will be further illustrated for the case where the halogen is chlorine, it should be understood that the invention applies to other halogens as well, such as fluorine, bromine and iodine. In the case of a catalyst containing chlorine, hydrochloric acid will form in the oxygenate to olefin reactor. HCl may be in the gas or condensed form, usually in a hydrated form, hereinafter referred to as HCl_((aq)). All forms of acids are potentially corrosive, the hydrated form being the most corrosive.

[0025] The invention addresses the problem associated with the use of inorganic oxide sols that contains halogen by removing much of the halogen from the catalyst during calcination of the catalyst. The invention addresses these problems by providing methods of heat treating or calcining a formed non-zeolitic molecular sieve catalyst prepared with an inorganic oxide sol that contains halogen. The methods of the invention minimize the production of halogen-containing acids, or at least confines much of the produced halogen-containing acids to a single heating or calcination unit that can be designed to accommodate the corrosive effects of halogen-containing acids. The methods of the invention also reduce the amount of halogen remaining in the catalyst over that of conventional procedures.

[0026] The catalyst is made by preparing a slurry containing non-zeolitic molecular sieve, an inorganic oxide binder, and a matrix material. The slurry is then dried and shaped in a forming unit. Preferably, the slurry is spray dried, and a dry powder catalyst with an average catalyst particle size is obtained. The formed catalyst is then heat treated, i.e., calcined.

[0027] Calcination is used to remove the template molecule from the cage structure of the framework. During calcination all or part of the template molecule exits the cage structure. Calcination is also used to harden the formed catalyst particle. The relatively high temperatures used during calcination transform the inorganic oxide sol to an inorganic oxide matrix. It is this inorganic oxide matrix that increases the attrition resistance of the catalyst particle.

[0028] If a conventional calcination procedure is used on a catalyst containing chlorine, that is, heating in air at temperatures greater than 400° C., large amounts of HCl are produced over time in the calcination unit. The formation of HCl_((aq)) is the result of small amounts of water or water vapor contained in the air and the water generated from the oxidative combustion of the organic template during calcination. The released HCl, if not accounted for, will eventually corrode the heating or calcination unit. Therefore, it is desirable to control the removal of chlorine from the catalyst in a manner that will either minimize the amount of HCl produced during the calcination process or limit the evolution of HCl to a single calcination unit.

[0029] A conventional calcination procedure also does not remove enough of the halogen from the catalyst. In the case of chlorine, the remaining chlorine in the catalyst is then released into the oxygenate to olefin reactor and other oxygenate to olefin process units as HCl_((aq)) due to the hydrothermal conditions of the oxygenate to olefin process. If not accounted for, the release of this HCl_((aq)) will corrode the oxygenate to olefin process units. The presence of HCl_((aq)) in the olefin monomer feed used for polymerization might also damage or poison expensive polymerization catalysts. Therefore, it is desirable to remove as much chlorine from the catalyst during the calcination process so as to minimize the amount of HCl_((aq)) released into the oxygenate to olefin process units.

[0030] As a result of using the calcination methods of the invention, a non-zeolitic molecular sieve catalyst with low amounts of halogen is obtained. A preferred catalyst of the invention contains a SAPO molecular sieve, an aluminum oxide matrix, and clay, most preferably Kaolin. The catalyst will also contain some halogen resulting from the use of a binder that contains halogen. Although the invention is directed to removing as much halogen from the catalyst as efficiently possible, some of the halogen is not removed during the calcination process. Following the calcination procedures of the invention, the catalyst will contain from about 10 ppmw to 600 ppmw halogen, preferably from about 10 ppmw to 200 ppmw halogen, more preferably from about 10 ppmw to 60 ppmw halogen. The catalyst will also have a Gross Attrition Loss (GAL) Index of less than 5, preferably a GAL Index less than 3, more preferably a GAL Index less than 2. The smaller the GAL Index, the more resistant to attrition is the catalyst.

[0031] Non Zeolitic Molecular Sieve

[0032] The catalyst used according to the present invention contains a non zeolitic molecular sieve. Examples of suitable non-zeolitic molecular sieves are silicoaluminophosphates (SAPOs) and aluminophosphates (ALPOs). In general, SAPO molecular sieves comprise a molecular framework of corner-sharing [SiO₄], [AlO₄], and [PO₄] tetrahedral units. The [PO₄] tetrahedral units are provided by a variety of compositions. Examples of these phosphorus-containing compositions include phosphoric acid, organic phosphates such as triethyl phosphate, and aluminophosphates. The [AlO₄] tetrahedral units are provided by a variety of compositions. Examples of these aluminum-containing compositions include aluminum alkoxides such as aluminum isopropoxide, aluminum phosphates, aluminum hydroxide, sodium aluminate, and pseudoboehmite. The [SiO₄] tetrahedral units are provided by a variety of compositions. Examples of these silicon-containing compositions include silica sols and silicium alkoxides such as tetra ethyl orthosilicate. The phosphorus-, aluminum-, and silicon-containing compositions are mixed with water and a template molecule and heated under appropriate conditions to form the molecular sieve.

[0033] SAPO molecular sieves are generally classified as being microporous materials having 8, 10, or 12 membered ring structures. These ring structures can have an average pore size ranging from about 3.5-15 angstroms. Preferred are the small pore SAPO molecular sieves having an average pore size of less than about 5 angstroms, preferably an average pore size ranging from about 3.5 to 5 angstroms, more preferably from 3.5 to 4.2 angstroms. These pore sizes are typical of molecular sieves having 8 membered rings.

[0034] An aluminophosphate (ALPO) molecular sieve can also be included in the catalyst composition. Aluminophosphate molecular sieves are crystalline microporous oxides which can have an AlPO₄ framework. They can have additional elements within the framework, typically have uniform pore dimensions ranging from about 3 Angstroms to about 10 Angstroms, and are capable of molecular size selective separations of molecular species. More than two dozen structure types have been reported, including zeolite topological analogues.

[0035] For a catalyst used in the conversion of oxygenate to light olefin the non-zeolitic molecular sieve will have a relatively low Si/Al₂ ratio. In general, for SAPOs, a Si/Al₂ ratio of less than 0.65 is desirable, with a Si/Al₂ ratio of not greater than 0.40 being preferred, and a Si/Al₂ ratio of not greater than 0.32 being particularly preferred. A Si/Al₂ ratio of not greater than 0.20 is most preferred.

[0036] Substituted SAPOs and ALPOs can also be used in this invention. These compounds are generally known as MeAPSOs, MeAPOs, metal-containing silicoaluminophosphates or metal-containing aluminophosphates. The metal can be alkali metal ions (Group IA), alkaline earth metal ions (Group IIA), rare earth ions (Group IIIB, including the lanthanide elements, and the additional transition cations of Groups IB, IIB, IVB, VB, VIB, VIIB, and VIIIB. Preferably, the Me represents atoms such as Zn, Ni, and Cu. These atoms can be inserted into the tetrahedral framework through a [MeO₂] tetrahedral unit. Incorporation of the metal component is typically accomplished by adding the metal component during synthesis of the molecular sieve. However, post-synthesis metal incorporation can also be used.

[0037] SAPO and ALPO molecular sieves that can be used include SAPO-5, SAPO-8, SAPO-11, SAPO-16, SAPO-17, SAPO-18, SAPO-20, SAPO-31, SAPO-34, SAPO-35, SAPO-36, SAPO-37, SAPO-40, SAPO-41, SAPO-42, SAPO-44, SAPO-47, SAPO-56, ALPO-5, ALPO-11, ALPO-18, ALPO-31, ALPO-34, ALPO-36, ALPO-37, ALPO-46, the metal containing forms thereof, and mixtures thereof. Preferred are SAPO-18, SAPO-34, SAPO-35, SAPO-44, SAPO-56, ALPO-18 and ALPO-34, particularly SAPO-18, SAPO-34, ALPO-34 and ALPO-18, including the metal containing forms thereof, and mixtures thereof. As used herein, the term mixture is synonymous with combination and is considered a composition of matter having two or more components in varying proportions, regardless of their physical state.

[0038] SAPO and ALPO molecular sieves are synthesized by hydrothermal crystallization methods generally known in the art. See, for example, U.S. Pat. Nos. 4,440,871; 4,861,743; 5,096,684; and 5,126,308, the disclosures of which are fully incorporated herein by reference. A reaction mixture is formed by mixing together reactive silicon, aluminum and phosphorus components, along with at least one template. Generally the mixture is sealed and heated, preferably under autogenous pressure, to a temperature of at least 100° C., preferably from 100-250° C., until a crystalline product is formed.

[0039] Formation of the crystalline product can take anywhere from around 2 hours to as much as 2 weeks. In some cases, stirring or seeding with crystalline material will facilitate the formation of the product. Typically, the molecular sieve product is formed in solution. It can be recovered by standard means, such as by centrifugation or filtration. The product can also be washed, recovered by the standard means, and dried. In one method, the molecular sieve is washed and collected by a filtration process that maintains the molecular sieve in slurry form. This process includes adding wash fluid as the molecular sieve is concentrated from the synthesis solution.

[0040] Additional molecular sieve materials can be included as a part of the non zeolitic catalyst or they can be used as separate molecular sieve catalysts in admixture with the non zeolitic molecular sieve catalyst if desired. Structural types of small pore molecular sieves that are suitable for use in this invention include AEI, AFT, APC, ATN, ATT, ATV, AWW, BIK, CAS, CHA, CHI, DAC, DDR, EDI, ERI, GOO, KFI, LEV, LOV, LTA, MON, PAU, PHI, RHO, ROG, THO, and substituted forms thereof. Structural types of medium pore molecular sieves that are suitable for use in this invention include MFI, MEL, MTW, EUO, MTT, HEU, FER, AFO, AEL, TON, and substituted forms thereof. These small and medium pore molecular sieves are described in greater detail in the Atlas of Zeolite Structural Types, W. M. Meier and D. H. Olsen, Butterworth Heineman, 3rd ed., 1997, the detailed description of which is explicitly incorporated herein by reference. Preferred molecular sieves which can be combined with a silicoaluminophosphate and/or an aluminophosphate catalyst include ZSM-5, ZSM-34, erionite, and chabazite.

[0041] Binders

[0042] Once the desired type or types of non-zeolitic molecular sieve is selected based upon the desired activity and selectivity of the catalyst, other materials are blended with the non-zeolitic molecular sieve. One of these materials includes one or more binders, such as a type of hydrated alumina, and/or an inorganic oxide sol such as aluminum chlorhydrol. The inorganic oxide sol is essentially a “glue” which binds the catalyst components together upon thermal treatment. After the formed catalyst particle is formed and heated, the inorganic oxide sol is converted to an inorganic oxide matrix component. For example, an alumina sol will convert to an aluminum oxide matrix following a heat treatment of the formed catalyst. Aluminum chlorhydrol is a hydroxylated aluminum based sol containing chloride as the counter ion. Aluminum chlorhydrol has the general formula of Al_(m)O_(n)(OH)_(o)Cl_(p).xH₂O wherein m is 1 to 20, n is 1 to 8, o is 5 to 40, p is 2 to 15, and x is 0 to 30. Although the equilibria of alumina species in the sol is complex, the predominant species is believed to be [Al₁₃O₄(OH)₂₄Cl₇(H₂O)₁₂]. In addition, other alumina materials may be added with the aluminum chlorhydrol. Materials that can be used include, but are not necessarily limited to aluminum oxyhydroxide, γ-alumina, boehmite, diaspore, and transitional aluminas such as α-alumina, β-alumina, γ-alumina, δ-alumina, ε-alumina, κ-alumina, and ρ-alumina. Aluminum trihydroxide, such as gibbsite, bayerite, nordstrandite, doyelite, and mixtures thereof, also can be used. A sufficient amount of the binder is added to the slurry mixture so that the amount of the resultant inorganic oxide matrix in the catalyst, not including the inorganic oxide framework of the non-zeolitic molecular sieve, is from about 2% to about 30% by weight, preferably from about 5% to about 20% by weight, and more preferably from about 7% to about 12% by weight.

[0043] Matrix Materials

[0044] The non zeolitic molecular sieve catalysts will also contain clay, preferably Kaolin. Matrix materials may also include compositions such as various forms of rare earth metals, metal oxides, titania, zirconia, magnesia, thoria, beryllia, quartz, silica or silica or silica sol, and mixtures thereof. The added matrix materials components are effective in reducing, inter alia, overall catalyst cost, acting as a thermal sink to assist in heat shielding the catalyst during regeneration, densifying the catalyst and increasing catalyst strength. The use of matrix materials such as naturally occurring clays, e.g., bentonite and kaolin, improves the crush strength of the catalyst under commercial operating conditions. Thus, the addition of clays improve upon the attrition resistance of the catalyst. The inactive materials also serve as diluents to control the rate of conversion in a given process so that more expensive means for controlling the rate of reaction is eliminated or minimized. Naturally occurring clays which can be used in the present invention include the montmorillonite and kaolin families which include the sabbentonites, and the kaolins, commonly known as Dixie, McNamee, Georgia and Florida clays, or other in which the main mineral constituent is haloysite, kaolinite, dickite, nacrite, or anauxite.

[0045] As with most catalysts clay is used in the invention as an inert densifier, and for the most part the clay has no effect on catalytic activity or selectivity. Kaolin's ability to form pumpable, high solid content slurries, low fresh surface area, and ease of packing because of its platelet structure makes it particularly suitable for catalyst processing. The preferred average particle size of the kaolin is 0.1 μm to 0.6 μm with a D90 particle size of about 1 μm. Because of environmental concerns, the crystalline silica content of the clay has also become an important parameter.

[0046] Mixing and Spray Drying.

[0047] Rigorous mixing of the catalyst components is necessary to produce a hard, dense, homogeneous catalyst particle. The primary consequence of poor mixing are poor attrition and poor catalyst density. Stratification of the components caused by incomplete mixing can also effect the activity and selectivity of the catalyst. Generally, the mixers are of a high shear type because of the thixotropic nature of the slurries. The resultant slurry may be colloid-milled for a period sufficient to obtain a desired sub-particle texture, sub-particle size, and/or sub-particle size distribution.

[0048] The catalyst particle contains a plurality of catalyst sub-particles. The average diameter of the catalyst particle is from 40 μm to 300 μm, preferably from 50 μm to 200 μm. The catalyst sub-particles contain non-zeolite molecular sieve, typically SAPO molecular sieve, an aluminum oxide matrix, and a matrix material, typically clay. Preparation of the catalyst begins with mixing one or more non-zeolite molecular sieve, one or more inorganic oxide sols, one or more matrix materials, and a fluid, typically water, to form a slurry. Other fluids, e.g., alcohol, can be used along with the water.

[0049] The preferred slurry is prepared by mixing the non-zeolitic molecular sieve with aluminum chlorhydrol and Kaolin clay, together or in sequence, in dry form or as slurries. If the solids are added together as dry solids, a limited and controlled amount of water is added. The slurry may also contain other materials including other forms of molecular sieve, other binders, and other matrix materials. The mesoporosity of the catalyst and the mechanical strength of the catalyst is dependent on the amount of water contained in the slurry. In general, it has been found that the weight percent of solids in the slurry can range from 20% to 70% by weight, preferably from 40% to 60% by weight. When the weight percent of solids in the slurry is greater than 70% by weight, the viscosity of the slurry is too high to spray dry, and when the weight percent of solids in the slurry is less than 20% by weight the attrition resistance of the catalyst is poor. It is also desirable that the density of the slurry be greater than 1.1 g/cc, and preferably greater than 1.18 g/cc to form the catalysts of this invention.

[0050] The solid content of the slurry will contain about 10% to about 50%, preferably from about 20% to about 45% by weight, non-zeolitic molecular sieve, about 5% to about 20%, preferably from about 8% to about 15% by weight, binder, and about 30% to about 80%, preferably about 40% to about 60% by weight, matrix material. The slurry is mixed or milled to achieve a sufficiently uniform slurry of catalyst sub-particles. The slurry is then fed to a forming unit to produce catalyst particles. The forming unit is maintained at a temperature sufficient to remove most of the water from the formed catalyst particles. Preferably, the forming unit is a spray dryer. The formed catalyst particles typically take the form of microspheres. Typically, the slurry is fed to a spray drier at an average inlet temperature ranging from 200° C. to 450° C., and an outlet temperature ranging from 100° C. to about 225° C.

[0051] During spray drying, the slurry is passed through a nozzle which distributes the slurry into small droplets, resembling an aerosol. A single nozzle unit or multiple nozzle unit may be used to disperse an inlet stream of slurry (single-fluid nozzle) into the atomization chamber. Alternatively, a multiple nozzles may be used to co-feed the slurry into the atomization chamber. Alternatively, the slurry is directed to the perimeter of a spinning wheel which also distributes the slurry into small droplets. The size of the distributed slurry droplets is controlled by many factors including flow rate, pressure, and temperature of the slurry, the shape and dimension of the nozzle(s), or the spinning rate of the wheel. The droplets are then dried in a co-current or counter-current flow of air passing through the spray drier. Dry catalyst particles in the form of a powder are recovered from each droplet.

[0052] Catalyst particle size to some extent is controlled by the solids content of the slurry and its viscosity. All else being equal, the catalyst particle size is directly proportional to the solids content of the slurry. However, control of the catalyst particle size and spherical characteristics also depend on the size and shape of the drying chamber as well as the atomization procedure used. A Boltzmann distribution of catalyst particle size is invariably obtained around a mean, which is usually set at approximately 70 μm average catalyst particle size. The average catalyst particle size is controlled by a variation in the slurry feed properties to the dryer and by the conditions of atomization. It is preferred that the formulated catalyst composition have a catalyst size from 40 μm to 300 μm, more preferably 50 μm to 200 μm, most preferably 50 μm to 150 μm.

[0053] Calcination.

[0054] To harden and/or activate the formed catalysts a heat treatment, i.e., calcination, at an elevated temperature is usually necessary. Ordinarily, catalysts with alumina or silica binders are heated in a calcination environment at a temperature between 500° C. and 800° C. The conventional calcination environment is air, which may include small amounts of water vapor.

[0055] The invention provides methods of heat treating a formed non-zeolitic molecular sieve catalyst prepared with an inorganic oxide sol that contains halogen. The methods of the invention minimize the production of halogen-containing acids or at least confines much of the produced halogen-containing acids to a single heating unit. The schematic diagram in FIG. 1 depicts one embodiment of the invention, in which a chlorine-containing SAPO catalyst 12 is used by way of example. Catalyst 12 is supplied from a forming unit, preferably a spray dryer, and is directed to a heat treatment unit 14. The catalyst is heated at a temperature from about 400° C. to about 1000° C., preferably from about 500° C. to about 800° C., most preferably from about 550° C. to about 700° C. in a low moisture calcination environment containing less than 5% by volume water, preferably less than 1% by volume water. The low moisture calcination environment can be provided by using a dry gas 18, e.g., air that has been adequately dried, nitrogen, helium, flue gas, or any combination thereof. In the preferred embodiment, the catalyst is heated in nitrogen off gas at a temperature from about 600° C. to about 700° C. Nitrogen off gas is the gas produced from the boil-off gas of a liquid nitrogen source. Heating is carried out for a period of time sufficient to remove chlorides, typically for a period of from 0.5 to 10 hours, preferably of from 1 to 5 hours, most preferably from 2 to 4 hours.

[0056] As the catalyst is heated in the low moisture calcination environment most of the chlorine is removed as chlorine gas or as a non-hydrated form of hydrochloric acid (HCl_((g))). HCl_((g)) is not as corrosive as HCl_((aq)). Approximately 60% to 98% by weight, preferably 85% to 98% by weight, of the chlorine in the formed catalyst 12 is removed during the heat treatment in the low moisture calcination environment. Following this heat treatment the catalyst 16 contains less than about 6000 ppmw chlorine, preferably less than about 3000 ppmw chlorine.

[0057] Following the low moisture heat treatment, the catalyst 16 is directed to heating unit 20. The catalyst in heating unit 20 is heated in a second calcination environment 24. This second calcination environment 24 contains from about 5% to about 10% by volume water. The remaining volume of gas in the calcination environment 24 may include air, nitrogen, helium, flue gas, or any combination thereof. The second heat treatment of the catalyst 16 will take place at a temperature from about 400° C. to about 1000° C., preferably from about 500° C. to about 800° C., more preferably from about 600° C. to about 700° C. The period during which the catalysts is heated in unit 20 ranges from 0.1 to 5 hours, preferably from 0.25 to 4 hours. This second heat treatment results in a loss of about 2% to about 95% of the chlorine remaining in catalyst 16. Catalyst 22 will contain less than about 600 ppmw chlorine, preferably less than about 200 ppmw chlorine, more preferably less than about 80 ppmw chlorine.

[0058] In another embodiment, the second calcination environment contains at least 10% by volume water. The remaining volume of gas in the second calcination environment may include air, nitrogen, helium, flue gas, or any combination thereof. Preferably, the second calcination environment contains air. A catalyst that is contacted with a calcination environment containing at least 10% by volume water is said to be steam-treated. Steam treatment results in a loss of about 50% to 99%, preferably in a loss of about 90% to about 99% of the chlorine remaining in the catalyst following the low moisture heat treatment. The steam-treated catalyst will contain about 10 ppmw to about 400 ppmw chlorine, preferably about 10 ppmw to about 200 ppmw chlorine, more preferably about 10 ppmw to about 80 ppmw chlorine.

[0059] Steam treatment of the catalyst will take place at a temperature from about 400° C. to about 1000° C., preferably from about 500° C. to about 800° C., more preferably from about 600° C. to about 700° C. The period during which the catalysts is heated in unit 20 ranges from 0.1 to 5 hours, preferably from 0.25 to 4 hours. Although temperatures of about 400° C. are sufficient to adequately remove most of the chlorine from the catalyst, the rate at which the additional chlorine is removed will be lower than if a higher temperature, e.g., 600° C., is used during steam treatment. On the other hand, if the temperature of the steam treatment is too high, e.g., greater than 1000° C., degradation of the catalyst may occur. The temperature at which degradation of the catalyst will occur will vary for different catalyst formulations and various non-zeolitic molecular sieve.

[0060] The low moisture heat treatment followed by steam treatment can remove about 70% to about 99.99% by weight, preferably about 95% to about 99.99% by weight, more preferably about 98% to about 99.99% by weight, of the chlorine in the formed catalyst. The steam treatment will produce HCl_((aq)), but the amount of HCl_((aq)) produced is significantly reduced because most of the chlorine is removed during the initial heat treatment in the low moisture calcination environment. As a result, the production of the HCl_((aq)) is minimized. Also, if separate heating units are used the production of HCl_((aq)) will be confined to the steam treatment unit, which can be designed to accommodate the HCl_((aq)) produced.

[0061] If air is not used in the steam treatment, the catalyst may be calcined in a calcination environment containing at least 3% by volume, preferably at least 10% by volume, oxygen to remove template material that may have remained in the pores of the sieve. A catalyst that has been calcined in an environment that contains at least 3% by volume oxygen is said to be oxygen treated. The oxygen environment may be provided by air or a mixture of air and nitrogen. The calcination temperature of this oxygen environment may be the same or different than the temperature of the steam treatment.

[0062] It is to be understood that although FIG. 1 depicts more than one heating unit for each type of heat treatment, a single heating unit may be used. In this case, the heating environment is changed by alternating the type of gas flow, e.g., from nitrogen off gas to steam, or from air to steam. Alternatively, different heating zones in a singular heating unit may be used according to the invention. Each heating zone will contain a different calcination environment with a transition zone disposed between the heating zones. The temperature and gas flow for each heating zone or heating unit can be programmed to minimize the time required to remove the desired amount of chlorine, while minimizing the amount of HCl_((aq)) produced. The heat and steam treatments may be done in any of a number of heating units well known to those skilled in the art including moving bed reactors, rotary kilns, rotary calciners, fluidized beds and packed-bed batch reactors.

[0063] In another embodiment the steam treatment is used to remove most of the halogen from the formed catalyst. Prior heating in a low moisture environment is not necessary. The formed catalyst is steam-treated at a temperature from about 400° C. to about 1000° C., preferably from about 500° C. to about 800° C., more preferably from about 600° C. to about 700° C. The period during which the catalysts is heated in unit 20 ranges from 0.1 to 5 hours, preferably from 0.25 to 4 hours. The steam treatment may remove from about 70% to about 99.99% by weight, preferably from about 95% to about 99.99% by weight, more preferably from about 98% to about 99.99% by weight, of the chlorine in the formed catalyst.

[0064] Following the steam treatment, the catalyst may be oxygen treated to remove template material that may have remained in the pores of the sieve. The calcination temperature of this oxygen environment may be the same or different than the temperature of the steam treatment.

[0065] In another embodiment, steam treatment of the catalyst may take place after an oxygen heat treatment. The catalyst is heated in an oxygen environment at a temperature from 400° C. to 1000° C., preferably from about 500° C. to about 800° C., more preferably from about 600° C. to about 700° C. The period during which the catalysts is heated in unit 20 ranges from 0.1 to 5 hours, preferably from 0.25 to 4 hours. Approximately 50% to 95% by weight, preferably 75% to 95% by weight, of the chlorine in the formed catalyst is removed during the oxygen heat treatment. The oxygen treated catalyst is then contacted with steam to remove additional amounts of chlorine from the catalyst. This steam contacted catalyst will contain about 10 ppmw to about 600 ppmw chlorine, preferably 10 ppmw to about 200 ppmw chlorine, more preferably 10 ppmw to about 80 ppmw chlorine.

[0066] The oxygen heat treatment and the steam treatment of the catalyst may take place in separate heating units or in the same heating unit though in different regions of that unit. For example, the oxygen environment may be introduced near the entrance to the heating unit and steam added near the middle of the heating unit. In this way partial calcination of the catalyst occurs prior to the catalyst contacting the steam.

[0067] The catalysts of the present invention are useful in a variety of processes including: cracking, hydrocracking, isomerization, polymerisation, reforming, hydrogenation, dehydrogenation, dewaxing, hydrodewaxing, absorption, alkylation, transalkylation, dealkylation, hydrodecylization, disproportionation, oligomerization, dehydrocyclization and combinations thereof. Due to the low level, or even absence of halogen in the non zeolitic catalyst, less corrosive acid is created during the catalytic process. Reactors may thus be used for longer periods of time before repair or replacement needs to take place.

[0068] The preferred processes of the present invention include a process directed to the conversion of a feedstock comprising one or more oxygenates to one or more olefin(s) and a process directed to the conversion of ammonia and one or more oxygenates to alkyl amines and in particular methylamines.

[0069] In a preferred embodiment of the process of the invention, the feedstock contains one or more oxygenates, more specifically, one or more organic compound(s) containing at least one oxygen atom. In the most preferred embodiment of the process of the invention, the oxygenate in the feedstock is one or more alcohol(s), preferably aliphatic alcohol(s) where the aliphatic moiety of the alcohol(s) has from 1 to 20 carbon atoms, preferably from 1 to 10 carbon atoms, and most preferably from 1 to 4 carbon atoms. The alcohols useful as feedstock in the process of the invention include lower straight and branched chain aliphatic alcohols and their unsaturated counterparts.

[0070] Non-limiting examples of oxygenates include methanol, ethanol, n-propanol, isopropanol, methyl ethyl ether, dimethyl ether, diethyl ether, di-isopropyl ether, formaldehyde, dimethyl carbonate, dimethyl ketone, acetic acid, and mixtures thereof.

[0071] In the most preferred embodiment, the feedstock is selected from one or more of methanol, ethanol, dimethyl ether, diethyl ether or a combination thereof, more preferably methanol and dimethyl ether, and most preferably methanol.

[0072] In the most preferred embodiment, the feedstock, preferably of one or more oxygenates, is converted in the presence of a catalyst into olefin(s) having 2 to 6 carbons atoms, preferably 2 to 4 carbon atoms. Most preferably, the olefin(s), alone or combination, are converted from a feedstock containing an oxygenate, preferably an alcohol, most preferably methanol, to the preferred olefin(s) ethylene and/or propylene.

[0073] The most preferred process is generally referred to as gas-to-olefins (GTO) or alternatively, methanol-to-olefins (MTO). In a MTO process, typically an oxygenated feedstock, most preferably a methanol containing feedstock, is converted in the presence of a catalyst into one or more olefin(s), preferably and predominantly, ethylene and/or propylene, often referred to as light olefin(s).

[0074] In one embodiment of the process for conversion of a feedstock, preferably a feedstock containing one or more oxygenates, the amount of olefin(s) produced based on the total weight of hydrocarbon produced is greater than 50 weight percent, preferably greater than 60 weight percent, more preferably greater than 70 weight percent.

[0075] The feedstock, in one embodiment, contains one or more diluent(s), typically used to reduce the concentration of the feedstock, and are generally non-reactive to the feedstock or catalyst. Non-limiting examples of diluents include helium, argon, nitrogen, carbon monoxide, carbon dioxide, water, essentially non-reactive paraffins (especially alkanes such as methane, ethane, and propane), essentially non-reactive aromatic compounds, and mixtures thereof. The most preferred diluents are water and nitrogen, with water being particularly preferred.

[0076] The diluent, water, is used either in a liquid or a vapour form, or a combination thereof. The diluent is either added directly to a feedstock entering into a reactor or added directly into a reactor, or added with a molecular sieve catalyst composition. In one embodiment, the amount of diluent in the feedstock is in the range of from about 1 to about 99 mole percent based on the total number of moles of the feedstock and diluent, preferably from about 1 to 80 mole percent, more preferably from about 5 to about 50, most preferably from about 5 to about 25. In one embodiment, other hydrocarbons are added to a feedstock either directly or indirectly, and include olefin(s), paraffin(s), aromatic(s) (see for example U.S. Pat. No. 4,677,242, addition of aromatics) or mixtures thereof, preferably propylene, butylene, pentylene, and other hydrocarbons having 4 or more carbon atoms, or mixtures thereof.

[0077] The process for converting a feedstock, especially a feedstock containing one or more oxygenates, in the presence of a catalyst of the invention, is carried out in a reaction process in a reactor, where the process is a fixed bed process, a fluidised bed process (includes a turbulent bed process), preferably a continuous fluidised bed process, and most preferably a continuous high velocity fluidised bed process.

[0078] The reaction processes can take place in a variety of catalytic reactors such as hybrid reactors that have a dense bed or fixed bed reaction zones and/or fast fluidised bed reaction zones coupled together, circulating fluidised bed reactors, riser reactors, and the like. Suitable conventional reactor types are described in for example U.S. Pat. No. 4,076,796, U.S. Pat. No. 6,287,522 (dual riser), and Fluidization Engineering, D. Kunii and O. Levenspiel, Robert E. Krieger Publishing Company, New York, N.Y. 1977, which are all herein fully incorporated by reference.

[0079] The preferred reactor type are riser reactors generally described in Riser Reactor, Fluidization and Fluid-Particle Systems, pages 48 to 59, F. A. Zenz and D. F. Othmo, Reinhold Publishing Corporation, New York, 1960, and U.S. Pat. No. 6,166,282 (fast-fluidised bed reactor), and U.S. patent application Ser. No. 09/564,613 filed May 4, 2000 (multiple riser reactor), which are all herein fully incorporated by reference.

[0080] In the preferred embodiment, a fluidised bed process or high velocity fluidised bed process includes a reactor system, a regeneration system and a recovery system.

[0081] The reactor system preferably is a fluid bed reactor system having a first reaction zone within one or more riser reactor(s) and a second reaction zone within at least one disengaging vessel, preferably comprising one or more cyclones. In one embodiment, the one or more riser reactor(s) and disengaging vessel is contained within a single reactor vessel. Fresh feedstock, preferably containing one or more oxygenates, optionally with one or more diluent(s), is fed to the one or more riser reactor(s) in which a catalyst or coked version thereof is introduced. In one embodiment, the catalyst or coked version thereof is contacted with a liquid or gas, or combination thereof, prior to being introduced to the riser reactor(s), preferably the liquid is water or methanol, and the gas is an inert gas such as nitrogen.

[0082] In an embodiment, the amount of fresh feedstock fed separately or jointly with a vapour feedstock, to a reactor system is in the range of from 0.1 weight percent to about 85 weight percent, preferably from about 1 weight percent to about 75 weight percent, more preferably from about 5 weight percent to about 65 weight percent based on the total weight of the feedstock including any diluent contained therein. The liquid and vapour feedstocks are preferably the same composition, or contain varying proportions of the same or different feedstock with the same or different diluent.

[0083] The feedstock entering the reactor system is preferably converted, partially or fully, in the first reactor zone into a gaseous effluent that enters the disengaging vessel along with a coked catalyst. In the preferred embodiment, cyclone(s) within the disengaging vessel are designed to separate the catalyst, preferably a coked catalyst, from the gaseous effluent containing one or more olefin(s) within the disengaging zone. Cyclones are preferred, however, gravity effects within the disengaging vessel will also separate the catalyst compositions from the gaseous effluent. Other methods for separating the catalyst compositions from the gaseous effluent include the use of plates, caps, elbows, and the like.

[0084] In one embodiment of the disengaging system, the disengaging system includes a disengaging vessel; typically a lower portion of the disengaging vessel is a stripping zone. In the stripping zone the coked catalyst is contacted with a gas, preferably one or a combination of steam, methane, carbon dioxide, carbon monoxide, hydrogen, or an inert gas such as argon, preferably steam, to recover adsorbed hydrocarbons from the coked catalyst that is then introduced to the regeneration system. In another embodiment, the stripping zone is in a separate vessel from the disengaging vessel and the gas is passed at a gas hourly superficial velocity (GHSV) of from 1 hr⁻¹ to about 20,000 hr⁻¹ based on the volume of gas to volume of coked catalyst, preferably at an elevated temperature from 250° C. to about 750° C., preferably from about 350° C. to 650° C., over the coked catalyst.

[0085] The conversion temperature employed in the conversion process, specifically within the reactor system, is in the range of from about 200° C. to about 1000° C., preferably from about 250° C. to about 800° C., more preferably from about 250° C. to about 750 ° C., yet more preferably from about 300° C. to about 650° C., yet even more preferably from about 350° C. to about 600° C. most preferably from about 350° C. to about 550° C.

[0086] The conversion pressure employed in the conversion process, specifically within the reactor system, varies over a wide range including autogenous pressure. The conversion pressure is based on the partial pressure of the feedstock exclusive of any diluent therein. Typically the conversion pressure employed in the process is in the range of from about 0.1 kPaa to about 5 MPaa, preferably from about 5 kPaa to about 1 MPaa, and most preferably from about 20 kPaa to about 500 kpaa.

[0087] The weight hourly space velocity (WHSV), particularly in a process for converting a feedstock containing one or more oxygenates in the presence of a catalyst within a reaction zone, is defined as the total weight of the feedstock excluding any diluents to the reaction zone per hour per weight of molecular sieve in the catalyst in the reaction zone. The WHSV is maintained at a level sufficient to keep the catalyst composition in a fluidised state within a reactor.

[0088] Typically, the WHSV ranges from about 1 hr⁻¹ to about 5000 hr⁻¹, preferably from about 2 hr⁻¹ to about 3000 hr⁻¹, more preferably from about 5 hr⁻¹ to about 1500 hr⁻¹, and most preferably from about 10 hr⁻¹ to about 1000 hr⁻¹. In one preferred embodiment, the WHSV is greater than 20 hr⁻¹; preferably the WHSV for conversion of a feedstock containing methanol and dimethyl ether is in the range of from about 20 hr⁻¹ to about 300 hr⁻¹.

[0089] The superficial gas velocity (SGV) of the feedstock including diluent and reaction products within the reactor system is preferably sufficient to fluidise the catalyst within a reaction zone in the reactor. The SGV in the process, particularly within the reactor system, more particularly within the riser reactor(s), is at least 0.1 meter per second (m/sec), preferably greater than 0.5 m/sec, more preferably greater than 1 m/sec, even more preferably greater than 2 m/sec, yet even more preferably greater than 3 m/sec, and most preferably greater than 4 m/sec. See for example U.S. patent application Ser. No. 09/708,753 filed Nov. 8, 2000, which is herein incorporated by reference.

[0090] In one preferred embodiment of the process for converting an oxygenate to olefin(s) using a silicoaluminophosphate catalyst, the process is operated at a WHSV of at least 20 hr⁻¹ and a Temperature Corrected Normalized Methane Selectivity (TCNMS) of less than 0.016, preferably less than or equal to 0.01. See for example U.S. Pat. No. 5,952,538, which is herein fully incorporated by reference.

[0091] In another embodiment of the processes for converting an oxygenate such as methanol to one or more olefin(s) using a catalyst, the WHSV is from 0.01 hr⁻¹ to about 100 hr⁻¹, at a temperature of from about 350° C. to 550° C., and silica to Me₂O₃ (Me is a Group IIIA or VIII element from the Periodic Table of Elements) molar ratio of from 300 to 2500. See for example EP-0 642 485 B1, which is herein fully incorporated by reference.

[0092] Other processes for converting an oxygenate such as methanol to one or more olefin(s) using a catalyst are described in PCT WO 01/23500 published Apr. 5, 2001 (propane reduction at an average catalyst feedstock exposure of at least 1.0), which is herein incorporated by reference.

[0093] The coked catalyst is withdrawn from the disengaging vessel, preferably by one or more cyclones(s), and introduced to the regeneration system. The regeneration system comprises a regenerator where the coked catalyst composition is contacted with a regeneration medium, preferably a gas containing oxygen, under general regeneration conditions of temperature, pressure and residence time.

[0094] Non-limiting examples of the regeneration medium include one or more of oxygen, O₃, SO₃, N₂O, NO, NO₂, N₂O₅, air, air diluted with nitrogen or carbon dioxide, oxygen and water (U.S. Pat. No. 6,245,703), carbon monoxide and/or hydrogen. The regeneration conditions are those capable of burning coke from the coked catalyst composition, preferably to a level less than 0.5 weight percent based on the total weight of the coked catalyst entering the regeneration system. The coked catalyst withdrawn from the regenerator forms a regenerated catalyst.

[0095] The regeneration temperature is in the range of from about 200° C. to about 1500° C., preferably from about 300° C. to about 1000° C., more preferably from about 450° C. to about 750° C., and most preferably from about 550° C. to 700° C. The regeneration pressure is in the range of from about 15 psia (103 kPaa) to about 500 psia (3448 kPaa), preferably from about 20 psia (138 kPaa) to about 250 psia (1724 kpaa), more preferably from about 25 psia (172 kPaa) to about 150 psia (1034 kPaa), and most preferably from about 30 psia (207 kPaa) to about 60 psia (414 kPaa).

[0096] The preferred residence time of the catalyst in the regenerator is in the range of from about one minute to several hours, most preferably about one minute to 100 minutes, and the preferred volume of oxygen in the gas is in the range of from about 0.01 mole percent to about 5 mole percent based on the total volume of the gas.

[0097] In one embodiment, regeneration promoters, typically metal containing compounds such as platinum, palladium and the like, are added to the regenerator directly, or indirectly, for example with the coked catalyst composition. Also, in another embodiment, a fresh catalyst is added to the regenerator containing a regeneration medium of oxygen and water as described in U.S. Pat. No. 6,245,703, which is herein fully incorporated by reference.

[0098] In an embodiment, a portion of the coked catalyst from the regenerator is returned directly to the one or more riser reactor(s), or indirectly, by pre-contacting with the feedstock, or contacting with fresh catalyst, or contacting with a regenerated catalyst or a cooled regenerated catalyst described below.

[0099] The burning of coke is an exothermic reaction, and in an embodiment, the temperature within the regeneration system is controlled by various techniques in the art including feeding a cooled gas to the regenerator vessel, operated either in a batch, continuous, or semi-continuous mode, or a combination thereof. A preferred technique involves withdrawing the regenerated catalyst from the regeneration system and passing the regenerated catalyst through a catalyst cooler that forms a cooled regenerated catalyst. The catalyst cooler, in an embodiment, is a heat exchanger that is located either internal or external to the regeneration system.

[0100] In one embodiment, the cooler regenerated catalyst is returned to the regenerator in a continuous cycle, alternatively, (see U.S. patent application Ser. No. 09/587,766 filed Jun. 6, 2000) a portion of the cooled regenerated catalyst is returned to the regenerator vessel in a continuous cycle, and another portion of the cooled molecular sieve regenerated catalyst is returned to the riser reactor(s), directly or indirectly, or a portion of the regenerated catalyst or cooled regenerated catalyst is contacted with by-products within the gaseous effluent (PCT WO 00/49106 published Aug. 24, 2000), which are all herein fully incorporated by reference. In another embodiment, a regenerated catalyst contacted with an alcohol, preferably ethanol, 1-propnaol, 1-butanol or mixture thereof, is introduced to the reactor system, as described in U.S. patent application Ser. No. 09/785,122 filed Feb. 16, 2001, which is herein fully incorporated by reference.

[0101] Other methods for operating a regeneration system are in disclosed U.S. Pat. No. 6,290,916 (controlling moisture), which is herein fully incorporated by reference.

[0102] The regenerated catalyst withdrawn from the regeneration system, preferably from the catalyst cooler, is combined with a fresh catalyst and/or re-circulated catalyst and/or feedstock and/or fresh gas or liquids, and returned to the riser reactor(s). In another embodiment, the regenerated catalyst withdrawn from the regeneration system is returned to the riser reactor(s) directly, preferably after passing through a catalyst cooler. In one embodiment, a carrier, such as an inert gas, feedstock vapour, steam or the like, semi-continuously or continuously, facilitates the introduction of the regenerated catalyst to the reactor system, preferably to the one or more riser reactor(s).

[0103] By controlling the flow of the regenerated catalyst or cooled regenerated catalyst from the regeneration system to the reactor system, the optimum level of coke on the catalyst entering the reactor is maintained. There are many techniques for controlling the flow of a catalyst described in Michael Louge, Experimental Techniques, Circulating Fluidised Beds, Grace, Avidan and Knowlton, eds. Blackie, 1997 (336-337), which is herein incorporated by reference.

[0104] Coke levels on the catalyst are measured by withdrawing from the conversion process the catalyst at a point in the process and determining its carbon content. Typical levels of coke on the catalyst, after regeneration is in the range of from 0.01 weight percent to about 15 weight percent, preferably from about 0.1 weight percent to about 10 weight percent, more preferably from about 0.2 weight percent to about 5 weight percent, and most preferably from about 0.3 weight percent to about 2 weight percent based on the total weight of the molecular sieve and not the total weight of the catalyst.

[0105] In one preferred embodiment, the mixture of fresh catalyst and regenerated catalyst and/or cooled regenerated catalyst contains in the range of from about 1 to 50 weight percent, preferably from about 2 to 30 weight percent, more preferably from about 2 to about 20 weight percent, and most preferably from about 2 to about 10 coke or carbonaceous deposit based on the total weight of the mixture of catalysts. See for example U.S. Pat. No. 6,023,005, which is herein fully incorporated by reference.

[0106] The gaseous effluent is withdrawn from the disengaging system and is passed through a recovery system. There are many well-known recovery systems, techniques and sequences that are useful in separating olefin(s) and purifying olefin(s) from the gaseous effluent. Recovery systems generally comprise one or more or a combination of a various separation, fractionation and/or distillation towers, columns, splitters, or trains, reaction systems such as ethylbenzene manufacture (U.S. Pat. No. 5,476,978) and other derivative processes such as aldehydes, ketones and ester manufacture (U.S. Pat. No. 5,675,041), and other associated equipment for example various condensers, heat exchangers, refrigeration systems or chill trains, compressors, knock-out drums or pots, pumps, and the like.

[0107] The metalloaluminophosphate molecular sieve materials and catalyst compositions of the present invention may be used in the manufacture of alkylamines, using ammonia. Examples of suitable processes are as described in published European patent application EP 0 993 867 A1, and in U.S. Pat. No. 6,153,798 to Hidaka et. al, which are herein fully incorporated by reference.

[0108] This invention will be better understood with reference to the following examples, which are intended to illustrate specific embodiments within the overall scope of the invention as claimed.

EXAMPLE 1

[0109] SAPO-34 molecular sieve, 50% by weight, aluminum chlorhydrol, 10% by weight, and UF grade kaolin clay, 40% by weight, was mixed with sufficient water to produce a slurry with approximately 40% by weight solids. The slurry was fed into a spray drier to form spray dried catalyst. The spray dried catalyst was analyzed by XRF (X-ray Fluorescence) spectroscopy. The amount of chlorine in the spray dried catalyst was 33,800 ppmw. The GAL Index of the un-calcined catalyst was greater than 50.

EXAMPLES 2-4

[0110] Spray dried catalyst of Example 1 was heated in a nitrogen stream at temperatures of 600° C., 650° C. and 700° C. for one hour. The heat treated catalyst was then analyzed by XRF to determine the amount of residual chlorine remaining in the catalyst. Table 1 lists the residual chlorine content of each catalyst.

EXAMPLES 5-7

[0111] Spray dried catalyst of Example 1 was heated in a nitrogen stream at temperatures of 600° C., 650° C. and 700° C. for nine hours. The heat treated catalysts were then analyzed by XRF to determine the amount of residual chlorine remaining in each catalyst. Table 1 lists the residual chlorine content of each catalyst.

EXAMPLES 8

[0112] Spray dried catalyst of Example 1 was heated in a nitrogen stream at temperatures of 650° C. for five hours followed by heating in air at 650° C. for two hours. The heat treated catalyst was then analyzed by XRF to determine the amount of residual chlorine remaining in the catalyst. The chlorine content of the catalyst was 390 ppm by weight.

EXAMPLES 9-11

[0113] The spray dried catalyst of Example 1 was heated in a nitrogen stream at temperatures of 600° C., 650° C. and 700° C. for one hour followed by heating in air at 600° C., 650° C. and 700° C. for one hour, respectively. The heat treated catalysts then analyzed by XRF to determine the amount of residual chlorine remaining catalyst. Table 1 lists the residual chlorine content of each catalyst. TABLE 1 Example Temperature, Sweep gas Sweep gas Chlorine, No. ° C. time, hrs time, hrs ppmw 1 n/a n/a n/a 33,800 2 600 N2/1 N/A 620 3 650 N2/1 N/A 520 4 700 N2/1 N/A 480 5 600 N2/9 N/A 440 6 650 N2/9 N/A 430 7 700 N2/9 N/A 350 8 650 N2/5 air/2 390 9 600 N2/1 air/1 510 10  650 N2/1 air/1 470 11  700 N2/1 air/1 430

EXAMPLE 12

[0114] The spray dried catalyst was heated at 600° C. in air for 120 minutes in an open container placed in an electrically heated muffle furnace. The calcined catalyst contained 1090 ppm chlorine (see Table 2).

EXAMPLE 13

[0115] The spray dried catalyst was heated at 650° C. in air for 120 minutes in an open container placed in an electrically heated muffle furnace. The calcined catalyst contained 730 ppm chlorine, and the GAL Index was 1.85 (see Table 2).

EXAMPLE 14

[0116] The spray dried catalyst was heated at 700° C. in air for 120 minutes in an open container placed in an electrically heated muffle furnace. The calcined catalyst contained 350 ppm chlorine (see Table 2).

EXAMPLE 15

[0117] The spray dried catalyst was heated at 600° C. in air for 120 minutes in an open container placed in an electrically heated muffle furnace. The calcined catalyst, 12 g, was placed in a ¾″ OD stainless steel, packed bed tubular reactor that was electrically heated. About 1 g/min of steam was fed to the reactor maintained at a temperature of 600° C. The catalyst was heated in the presence of steam for 120 minutes. The chlorine content of the treated catalyst was 250 ppm (see Table 2).

EXAMPLE 16

[0118] The same procedure as in Example 15 was used except that the temperature was maintained at 650° C. for both the heating in air and heating in steam. The chlorine content of the treated catalyst was 140 ppm, and the GAL Index was 1.48 (see Table 2).

EXAMPLE 17

[0119] The same procedure as in Example 15 was used except that the temperature was maintained at 700° C. for both the heating in air and heating in steam. The chlorine content of the treated catalyst was 30 ppm (see Table 2).

EXAMPLE 18

[0120] The same procedure as in Examples 12 was used except that the catalyst was heated in air for 240 minutes. The chlorine content of the treated catalyst was 830 ppm (see Table 2).

EXAMPLE 19

[0121] The same procedure as in Examples 13 was used except that the catalyst was heated in air for 240 minutes. The chlorine content of the treated catalyst was 590 ppm (see Table 2).

EXAMPLE 20

[0122] The same procedure as in Examples 14 was used except that the catalyst was heated in air for 240 minutes. The chlorine content of the treated catalyst was 290 ppm (see Table 2).

EXAMPLES 21-26

[0123] The same procedure as in Examples 15 were used except the times and temperatures of heating in air and the times and temperatures of heating in steam as indicated in Table 2.

EXAMPLE 27

[0124] The spray dried catalyst was heated at 600° C. in air for 120 minutes in an open container placed in an electrically heated muffle furnace. The calcined catalyst then placed in a ¾″ OD stainless steel, packed bed tubular reactor that was electrically heated. About 1 g/min of steam at about 1 atm was fed to the reactor maintained at a temperature of 600° C. The catalyst was heated in the presence of steam for 240 minutes. The chlorine content of the treated catalyst was 150 ppmw, and the GAL Index was 2.24 (see Table 2).

EXAMPLE 28

[0125] The same procedure as in Example 27 was used except the temperatures of heating in air and the steam treatment was 650° C. The chlorine content of the treated catalyst was 40 ppmw, and the GAL Index was 1.62 (see Table 2).

[0126] As summarized in Table 2, heating in air for 120 minutes at 600° C., 650° C. and 700° C. without a subsequent steam treatment reduces the chlorine content to 1090, 730 or 350 ppm respectively. Increasing the heating time to 240 minutes at 600° C., 650° C. and 700° C., results in the further reduction in chlorine content to 830, 590 or 290 ppm, respectively. As indicated only small amounts of additional chlorine is removed by a doubling of the heating time. For example, heating at 650° C. during the first 120 minutes reduces the chlorine content in the catalyst by about 98%, i.e., from 33,800 ppm to 730 ppm. Heating for a second 120 minutes reduces the remaining chlorine content by an additional 19%, i.e., from 730 ppm to 590 ppm.

[0127] Heating in air for 120 minutes followed by heating in the presence of steam for 120 minutes at temperatures of 600° C., 650° C., and 700° C. reduces the chlorine content to 250, 140 and 30 ppm, respectively. Increasing the time the catalyst is heated in air and steam to 240 minutes, respectively, has little affect on further reducing the chlorine content as shown by a comparison of Examples 15-17 with Examples 21-23, respectively.

[0128] Examples 24-26 indicate that increasing the time the catalyst is steam treated at a given temperature (650° C. in these examples) following the heat treatment in air for 120 minutes results in a yet greater reduction in chlorine content. The most dramatic reduction in chlorine content is made during the first 15 minutes of contacting the heat treated catalyst with steam. For example, comparison of Example 13 with Example 24 suggests that the chlorine content is reduced from 730 ppm to 230 ppm after an additional 15 minute steam treatment at 650° C. This amounts to an additional chlorine reduction of about 68%. Also, as indicated in Table 2 greater than 99% of the chlorine may be removed from the catalyst following the steam treatment of the catalyst. TABLE 2 Time Time Example (air) (steam) GAL Chlorine No. Temp. ° C. min. min. Index Ppmw 1 N/A N/A N/A >50 33800 12 600 120 0 1090 13 650 120 0 1.85 730 14 700 120 0 350 15 600 120 120 250 16 650 120 120 1.48 140 17 700 120 120 30 18 600 240 0 830 19 650 240 0 590 20 700 240 0 290 21 600 240 240 220 22 650 240 240 160 23 700 240 240 40 24 650 120 15 230 25 650 120 30 120 26 650 120 60 70 27 600 120 240 2.24 150 28 650 120 240 1.62 40

[0129] The attrition properties of Examples 1, 13, 16, 27, and 28 are listed in Table 2. Attrition properties of catalysts can be defined by the Gross Attrition Loss (GAL) Index. The smaller the GAL Index the more resistant to attrition is the catalyst. The GAL Index is measured in the following manner. About 6.0±0.1 g of SAPO catalyst was added to an attrition cup of an attrition apparatus known in the art. 23,700 scc/min of nitrogen gas was bubbled through a water-containing bubbler to humidify the N₂. The wet nitrogen passed through the attrition cup and exited the attrition apparatus through a porous fiber thimble. This thimble separates the fine catalyst particles resulting from the attrition of the catalyst particles in the attrition cup as the catalyst particles are circulated in the attrition cup by the fast flowing nitrogen gas. The pore size of the thimble determines the size of the fine particles that are separated from the catalyst. The pore size of the thimble used to measure the GAL Index was less than about 2 μm.

[0130] The nitrogen flow passing through the attrition cup was maintained for 60 minutes. The contents of the attrition cup were transferred to an elutriation cup. The elutriation cup is designed not to cause further attrition of the catalyst particles, but to remove any fine particles remaining in the attrition cup so that the fine particles may be included in the GAL Index. 23,700 scc/min of nitrogen gas was passed through the elutriation cup for 30 minutes. Additional fine particles were separated by the thimble. The collection of fine SAPO particles separated by the thimble were weighed. The amount in grams of fine particles divided by the original amount of catalyst added to the attrition cup is the GAL Index.

GAL Index=C/(B+C)×100

[0131] wherein

[0132] B=weight of catalyst in elutriation cup

[0133] C=weight of collected fine catalyst particles

[0134] Having now fully described this invention, it will be appreciated by those skilled in the art that the invention can be performed within a wide range of parameters within what is claimed, without departing from the spirit and scope of the invention. 

1. A hydrocarbon conversion process comprising the steps of: (a) introducing a feedstock to a reactor system in the presence of a catalyst comprising a non zeolitic molecular sieve, inorganic oxide matrix, and matrix material, wherein the catalyst contains from 10 ppm to 600 ppm by weight halogen; (b) withdrawing from the reactor system an effluent stream; and (c) passing the effluent gas through a recovery system recovering at least the one or more conversion products.
 2. The process of claim 1 wherein the feedstock comprises one or more oxygenates.
 3. The process of claim 2 wherein the one or more oxygenates comprises methanol.
 4. The process of claim 1 wherein the one or more conversion products comprises one or more olefins.
 5. The process of claim 4 wherein the one or more olefins comprises ethylene, propylene and mixtures thereof.
 6. The process of claim 1 wherein the feedstock comprises one or more oxygenates and ammonia.
 7. The process of claim 6 wherein the one or more conversion products comprises one or more alkylamines.
 8. The process of claim 7 wherein the one or more alkylamines comprises one or more methylamines.
 9. The process of claim 6 wherein the one or more oxygenates comprises methanol.
 10. The process of claim 1 wherein the feedstock comprises one or more oxygenates and one or more aromatic compound.
 11. The process of claim 10 wherein the one or more conversion products comprises one or more alkylated aromatic compound.
 12. The process of claim 1 wherein the conversion process is cracking.
 13. The process of claim 1 wherein the conversion process is dewaxing.
 14. The process of claim 1 wherein the halogen is chlorine.
 15. The process of claim 14 wherein the catalyst contains from 10 ppmw to 400 ppmw chlorine.
 16. The process of claim 14 wherein the catalyst contains from 10 ppmw to 200 ppmw chlorine.
 17. The process of claim 15 wherein the catalyst contains from 10 ppmw to 80 ppmw chlorine.
 18. The process of claim 1 wherein the catalyst has a GAL Index of less than
 5. 19. The process of claim 18 wherein the GAL Index is less than
 3. 20. The process of claim 1 wherein the non-zeolitic molecular sieve is selected from SAPO-5, SAPO-8, SAPO-11, SAPO-16, SAPO-17, SAPO-18, SAPO-20, SAPO-31, SAPO-34, SAPO-35, SAPO-36, SAPO-37, SAPO-40, SAPO-41, SAPO-42, SAPO-44, SAPO-47, SAPO-56, ALPO-5, ALPO-11, ALPO-18, ALPO-31, ALPO-34, ALPO-36, ALPO-37, ALPO-46, the metal containing forms of each thereof, and mixtures thereof.
 21. The process of claim 1 wherein the catalyst comprises 20% to 45% by weight non-zeolitic molecular sieve, 5% to 20% by weight of inorganic oxide matrix, and 20% to 70% by weight matrix material.
 22. The process of claim 21 wherein the catalyst comprises 25% to 42% by weight non-zeolitic molecular sieve, 8% to 15% by weight of inorganic oxide matrix, and 40% to 60% by weight matrix material.
 23. The process of claim 19 wherein the GAL Index is less than
 2. 24. The process of claim 1 wherein the inorganic oxide matrix comprises an aluminum oxide matrix.
 25. The process of claim 2 wherein the source of chlorine is aluminum chlohydrol.
 26. A hydrocarbon conversion process comprising the steps of: (a) providing a halogen-containing non-zeolitic molecular sieve catalyst; (b) heating the catalyst in a low moisture environment at a temperature from 400° C. to 1000° C.; (c) contacting the heated catalyst with steam at a temperature from 400° C. to 1000° C. to produce a steam-treated catalyst; (d) introducing a feedstock to a reactor system in the presence of the steam-treated catalyst obtained at step (c); (e) withdrawing from the reactor system an effluent stream; and (f) passing the effluent gas through a recovery system recovering at least the one or more conversion products.
 27. The process of claim 26 wherein the halogen is chlorine.
 28. The process of claim 26 wherein the feedstock comprises one or more oxygenates.
 29. The process of claim 28 wherein the one or more oxygenates comprises methanol.
 30. The process of claim 26 wherein the one or more conversion products comprises one or more olefins.
 31. The process of claim 30 wherein the one or more olefins comprises ethylene, propylene and mixtures thereof.
 32. The process of claim 26 wherein the feedstock comprises one or more oxygenates and ammonia.
 33. The process of claim 32 wherein the one or more conversion products comprises one or more alkylamines.
 34. The process of claim 33 wherein the one or more alkylamines comprises one or more methylamines.
 35. The process of claim 32 wherein the one or more oxygenates comprises methanol.
 36. The process of claim 26 wherein the feedstock comprises one or more oxygenates and one or more aromatic compound.
 37. The process of claim 36 wherein the one or more conversion products comprises one or more alkylated aromatic compound.
 38. The process of claim 26 wherein the conversion process is cracking.
 39. The process of claim 26 wherein the conversion process is dewaxing.
 40. A hydrocarbon conversion process comprising the steps of: (a) providing a halogen-containing non-zeolitic molecular sieve catalyst; (b) heating the catalyst in an oxygen environment at a temperature from 400° C. to 1000° C.; (c) contacting the heated catalyst with steam at a temperature from 400° C. to 1000° C. to produce a steam-treated catalyst; (d) introducing a feedstock to a reactor system in the presence of the steam-treated catalyst obtained at step (c); (e) withdrawing from the reactor system an effluent stream; and (f) passing the effluent gas through a recovery system recovering at least the one or more conversion products.
 41. The process of claim 40 wherein the halogen is chlorine.
 42. The process of claim 40 wherein the feedstock comprises one or more oxygenates.
 43. The process of claim 42 wherein the one or more oxygenates comprises methanol.
 44. The process of claim 40 wherein the one or more conversion products comprises one or more olefins.
 45. The process of claim 44 wherein the one or more olefins comprises ethylene, propylene and mixtures thereof.
 46. The process of claim 40 wherein the feedstock comprises one or more oxygenates and ammonia.
 47. The process of claim 46 wherein the one or more conversion products comprises one or more alkylamines.
 48. The process of claim 47 wherein the one or more alkylamines comprises one or more methylamines.
 49. The process of claim 46 wherein the one or more oxygenates comprises methanol.
 50. The process of claim 40 wherein the feedstock comprises one or more oxygenates and one or more aromatic compound.
 51. The process of claim 50 wherein the one or more conversion products comprises one or more alkylated aromatic compound.
 52. The process of claim 40 wherein the conversion process is cracking.
 53. The process of claim 40 wherein the conversion process is dewaxing.
 54. A hydrocarbon conversion process comprising the steps of: (a) providing a halogen-containing non-zeolitic molecular sieve catalyst; (b) heating the catalyst in an environment containing steam at a temperature from 400° C. to 1000° C.; (c) removing from 70% to 99.99% by weight of the halogen from the catalyst, thereby producing a steam-treated catalyst; (d) introducing a feedstock to a reactor system in the presence of the steam-treated catalyst obtained at step (c); (e) withdrawing from the reactor system an effluent stream; and (f) passing the effluent gas through a recovery system recovering at least the one or more conversion products.
 55. The process of claim 54 wherein the halogen is chlorine.
 56. The process of claim 54 wherein the feedstock comprises one or more oxygenates.
 57. The process of claim 56 wherein the one or more oxygenates comprises methanol.
 58. The process of claim 54 wherein the one or more conversion products comprises one or more olefins.
 59. The process of claim 58 wherein the one or more olefins comprises ethylene, propylene and mixtures thereof.
 60. The process of claim 54 wherein the feedstock comprises one or more oxygenates and ammonia.
 61. The process of claim 60 wherein the one or more conversion products comprises one or more alkylamines.
 62. The process of claim 61 wherein the one or more alkylamines comprises one or more methylamines.
 63. The process of claim 60 wherein the one or more oxygenates comprises methanol.
 64. The process of claim 54 wherein the feedstock comprises one or more oxygenates and one or more aromatic compound.
 65. The process of claim 64 wherein the one or more conversion products comprises one or more alkylated aromatic compound.
 66. The process of claim 54 wherein the conversion process is cracking.
 67. The process of claim 54 wherein the conversion process is dewaxing. 